CHIMEI HIPS PH-888C — High Gloss Impact Polystyrene Resin
CHIMEI HIPS PH-888C is a high-impact polystyrene resin supplied in pellet form for injection molding. This grade is reported to combine high gloss, impact performance and heat resistance for molded appliance, electrical and engineering components.With reported melt flow rates of 3.1–3.5 g/10 min, density of 1.05 g/cm³ and Vicat softening point of 103°C, HIPS PH-888C can be evaluated for applications requiring a balanced combination of appearance, stiffness and impact resistance.
Key Features
- High-impact polystyrene resin in pellet form
- Reported high-gloss surface characteristics
- Designed for injection molding evaluation
- Reported heat resistance and impact performance
- Suitable for appliance and electrical-component projects
Typical Technical Data
| Property | Reported Value | Test Method |
|---|---|---|
| Melt Flow Rate | 3.1 g/10 min, 200°C/10 kg | ISO 1133 |
| Melt Flow Rate | 3.5 g/10 min, 200°C/5 kg | ASTM D1238 |
| Density | 1.05 g/cm³ | ASTM D792 |
| Rockwell Hardness | L-85 | ASTM D785 |
| Tensile Strength | 330 kg/cm² | ASTM D638 |
| Notched Izod Impact Strength | 12.5 kg-cm/cm at 1/8 in | ASTM D256 |
| Notched Izod Impact Strength | 9.0 kg-cm/cm at 1/4 in | ASTM D256 |
| Flexural Strength | 480 kg/cm² | ASTM D790 |
| Heat Deflection Temperature, Annealed | 95°C | ASTM D648 |
| Heat Deflection Temperature, Unannealed | 82°C | ASTM D648 |
| Vicat Softening Point | 103°C | ASTM D1525 |
| Elongation at Break | 40% | ASTM D638 |
| Flammability | 1/16 in HB, reported | UL 94 |
High Gloss HIPS for Injection Molding
HIPS PH-888C can be evaluated for injection-molded parts where surface appearance, impact resistance and thermal performance are relevant. Process settings should be optimized according to equipment, mold design, part geometry and finished-product requirements.
Reported Application Areas
This grade may be evaluated for:
- Household-appliance components
- Electrical and electronic parts
- Instrument housings and engineering components
- General-purpose high-gloss injection-molded products
Product Identification
This material may be referenced in RFQs and technical specifications as:
- CHIMEI HIPS PH-888C
- HIPS PH-888C Resin
- High Gloss HIPS Resin
- High Impact Polystyrene Pellets
- Injection Molding HIPS
Request Current Lot Documentation
Contact Lema Plastic for availability, packaging, lead time and quotation. Please provide your intended application, processing method and destination market when requesting current TDS, SDS and COA documentation.
Continue browsing
More products from the catalog
Pair it with other pieces from the same collection or routine.
HIPS 622 Resin | High Impact Polystyrene Pellets for Injection Molding
HIPS 622 high impact polystyrene resin with reported MFR 4.8 g/10 min, density 1.03 g/cm³ and HDT 80°C. Pellets for injection molding.
View productPS Resin
GPPS GON525 Resin | Transparent Polystyrene Pellets
GPPS GON525 transparent polystyrene resin with reported MVR 6–10 cm³/10 min, 89.7% transmittance and 83.3°C HDT. Pellets for injection molding.
View productPS Resin
GPPS Resin GP-525 | Transparent Polystyrene Pellets
GPPS resin GP-525: transparent general-purpose polystyrene pellets for injection molding. Reported MFR 5–10 g/10 min, 40 MPa tensile, Vicat ≥92 °C.